Water-Accelerated Photo-oxidation of CH3NH3PbI3 Perovskite: Mechanism, rate orders, and rate constants
Timothy Siegler, Wiley Dunlap-Shohl, Yuhuan Meng, Wylie Kau, Preetham Sunkari, Chang-En Tsai,Zachary Armstrong, Yu-Chia Chen, David Beck, Marina Meila, and Hugh Hillhouse
arXiv, 2021
Abstract
Optical absorbance is used to study the kinetics of methylammonium lead iodide (MAPbI3) thin film degradation in response to combinations of moisture, oxygen, and illumination over a range of temperatures. 105 degradations were conducted over 41 unique environmental conditions. We discover that water acts synergistically with oxygen in a water-accelerated photo-oxidation (WPO) pathway. This pathway is the dominant pathway at 25 $^\circ$C and is 10, 100, 1000, and >1000 times faster than dry photooxidation (DPO), degradation via hydrate formation, thermal degradation, and blue light degradation, respectively. We find that the rate determining step for DPO is proton abstraction from methylammonium while for WPO it is proton abstraction from water, which occurs at a faster rate and results in water acting as an accelerant for photooxidation of MAPbI3. A full kinetic rate equation is derived and fitted to the data to determine activation energies and rate constants.
Bibtex
Recommended citation
Timothy Siegler, Wiley Dunlap-Shohl, Yuhuan Meng, Wylie Kau, Preetham Sunkari, Chang-En Tsai,Zachary Armstrong, Yu-Chia Chen, David Beck, Marina Meila, and Hugh Hillhouse. Water-Accelerated Photo-oxidation of CH3NH3PbI3 Perovskite: Mechanism, rate orders, and rate constants. ChemRxiv, June 2021